Microstructure and mechanical properties of laser beam welded Al–Li alloy 2060 with Al–Mg filler wire

Alloy 2060-T8 is a newly developed high-strength Al–Li alloy for applications in aircraft industry. Crack-free welds were obtained in laser beam welding with 5087 filler wire under optimized welding conditions. In this paper, fusion zone microstructure and joint mechanical properties were investigated. Microstructure typical for the weld metal consists of α-Al matrix with a few nanoscale precipitates inside and a coarse icosahedral quasicrystalline T₂ phase at the dendritic and grain boundaries. The quasicrystalline occurred normally in Al–Li–Cu alloys with higher Li contents. Our investigations show that the icosahedral quasicrystalline phase T₂ phase forms in the laser-welded Al–Li alloy 2060 with lower Li content as a result of segregation and replacement of Mg element. The joint tensile strength in as-welded condition is around 317 MPa, about 63% of that of the base metal, and fracture occurs within the fusion zone.     

Real-time measurements of temperature,pressure and moisture profiles in High-Performance Concrete exposed to high temperatures during neutron radiography imaging

High-Performance Concrete (HPC) is particularly prone to explosive spalling when exposed to high temperature. Although the exact causes that lead to spalling are still being debated, moisture transport during heating plays an important role in all proposed mechanisms. In this study, slabs made of high-performance, low water-to-binder ratio mortars with addition of superabsorbent polymers (SAP) and polypropylene fibers (PP) were heated from one side on a temperature-controlled plate up to 550 °C. A combination of measurements was performed simultaneously on the same sample: moisture profiles via neutron radiography, temperature profiles with embedded thermocouples and pore pressure evolution with embedded pressure sensors. Spalling occurred in the sample with SAP, where sharp profiles of moisture and temperature were observed. No spalling occurred when PP-fibers were introduced in addition to SAP. The experimental procedure described here is essential for developing and verifying numerical models and studying measures against fire spalling risk in HPC.     

Ni2V2O7 dandelion microsphere for a high-performance electrocatalyst in water splitting

Water splitting is an effective way to produce hydrogen to solve the energy crisis problem, and inorganic metal compounds are widely used in electrocatalysis field due to efficient hydrogen evolution reaction (HER). Herein, we synthesize Ni₂V₂O₇ dandelion microsphere from nickel nitrate and vanadium pentoxide by “one-step hydrothermal” way, which exhibits large specific surface area of 102.74 m² g⁻¹. The as-prepared Ni₂V₂O₇ microsphere shows good electrocatalysis performances including OER overpotential of 358 mV and good stability, as well as HER overpotential of 195 mV. Furthermore, the Ni₂V₂O₇ microsphere electrode is assembled to Ni₂V₂O₇ microsphere//Ni₂V₂O₇ microsphere system, showing the water splitting voltage of 1.50 V at 10 mA cm⁻² by two-electrode method, which is much lower than those of commercial RuO₂//Pt/C system and most of spinel oxides electrocatalysts. Our work opens up a new and facile avenue for fabricating inorganic microsphere electrocatalyst in hydrogen production field.     

Low-temperature hot-press sintering of AlN ceramics with MgO–CaO–Al2O3–SiO2 glass additives for ceramic heater applications

Aluminum nitride (AlN) is used a ceramic heater material for the semiconductor industry. Because extremely high temperatures are required to achieve dense AlN components, sintering aids such as Y₂O₃ are typically added to reduce the sintering temperature and time. To further reduce the sintering temperature, in this study, a low-melting-temperature glass (MgO–CaO–Al₂O₃–SiO₂; MCAS) was used as a sintering additive for AlN. With MCAS addition, fully dense AlN was obtained by hot-press sintering at 1500 °C for 3 h at 30 MPa. The mechanical properties, thermal conductivity, and volume resistance of the sintered AlN–MCAS sample were evaluated and compared with those of a reference sample (AlN prepared with 5 wt% Y2O3 sintering aid sintered at 1750 °C for 8 h at 10 MPa). The thermal conductivity of AlN prepared with 0.5 wt% MCAS was 91.2 W/m?K, which was 84.8 W/m?K lower than that of the reference sample at 25 °C; however, the difference in thermal conductivity between the samples was only 14.2 W/m?K at the ceramic-heater operating temperature of 500 °C. The flexural strength of AlN–MCAS was 550 MPa, which was higher than that of the reference sample (425 MPa); this was attributed to the smaller grain size achieved by low-temperature sintering. The volume resistance of AlN–MCAS was lower than that of the reference sample in the range of 200–400 °C. However, the resistivity of the proposed AlN–MCAS sample was higher than that of the reference sample (500 °C) owing to grain-boundary scattering of phonons. In summary, the proposed sintering strategy produces AlN materials for heater applications with low production cost, while achieving the properties required by the semiconductor industry.     

Role of additives in fabrication of soy-based rigid polyurethane foam for structural and thermal insulation applications

Environmental concerns continue to pose the challenge to replace petroleum-based products with renewable ones completely or at least partially while maintaining comparable properties. Herein, rigid polyurethane (PU) foams were prepared using soy-based polyol for structural and thermal insulation applications. Cell size, density, thermal resistivity, and compression force deflection (CFD) values were evaluated and compared with that of petroleum-based PU foam Baydur 683. The roles of different additives, that is, catalyst, blowing agent, surfactants, and different functionalities of polyol on the properties of fabricated foam were also investigated. For this study, dibutyltin dilaurate was employed as catalyst and water as environment friendly blowing agent. Their competitive effect on density and cell size of the PU foams were evaluated. Five different silicone-based surfactants were employed to study the effect of surface tension on cell size of foam. It was also found that 5 g of surfactant per 100 g of polyol produced a foam with minimum surface tension and highest thermal resistivity (R value: 26.11 m²·K/W). However, CFD values were compromised for higher surfactant loading. Additionally, blending of 5 g of higher functionality soy-based polyol improved the CFD values to 328.19 kPa, which was comparable to that of petroleum-based foam Baydur 683.     

A zirconium-free glaze system for sanitary ceramics with SiO2-CaCO3-TiO2 composite opacifier containing anatase: Effect of interface combination among SiO2, CaCO3 and TiO2

TiO₂ is an ideal substitute to ZrSiO₄ ceramic opacifier, yet it is limited to application because of the undesirable yellowing resulting from rutile formation. Herein, the SiO₂-CaCO₃-TiO₂ composite opacifier (Si-Ca-Ti) was constructed. The glaze used Si-Ca-Ti presents a superior opacification performance than ZrSiO₄ opacified glaze without causing yellowing, showing L*, a*, b* values of 94.81, -0.67 and 3.23. By comparison, the glaze using SiO₂, CaCO₃, and TiO₂ mixture shows lower opacification and yellowish surface with L* and b* values of 92.99 and 5.36. It is revealed that there is a close interface bonding among SiO₂, CaCO₃ and TiO₂ in Si-Ca-Ti, which promotes their combination reaction to generate opacification phase titanite and inhibit rutile formation when sintering, resulting in the white surface and opacification improvement of the glaze. This study proposes a green and efficient strategy to achieve white and highly opacified glaze for sanitary ceramics, exhibiting good application prospect.     

Hydrogen from wet air and sunlight in a tandem photoelectrochemical cell

A solid-state photoelectrochemical (SSPEC) cell is an attractive approach for solar water splitting, especially when it comes to monolithic device design. In a SSPEC cell the electrodes distance is minimized, while the use of polymer-based membranes alleviates the need for liquid electrolytes, and at the same time they can separate the anode from the cathode. In this work, we have made and tested, firstly, a SSPEC cell with a Pt/C electrocatalyst as the cathode electrode, under purely gaseous conditions. The anode was supplied with air of 80% relative humidity (RH) and the cathode with argon. Secondly, we replaced the Pt/C cathode with a photocathode consisting of 2D photocatalytic g-C₃N₄, which was placed in tandem with the photoanode (tandem-SSPEC). The tandem configuration showed a three-fold enhancement in the obtained photovoltage and a steady-state photocurrent density. The mechanism of operation is discussed in view of recent advances in surface proton conduction in absorbed water layers. The presented SSPEC cell is based on earth-abundant materials and provides a way towards systems of artificial photosynthesis, especially for areas where water sources are scarce and electrical grid infrastructure is limited or nonexistent. The only requirements to make hydrogen are humidity and sunlight.     

Structure and phase-composition of Ti-doped gas atomized Raney-type Ni catalyst precursor alloys

Raney-type Ni precursor alloys containing 75 at.% Al and doped with 0, 0.75, 1.5 and 3.0 at.% Ti have been produced by a gas atomization process. The resulting powders have been classified by size fraction with subsequent investigation by powder XRD, SEM and EDX analysis. The undoped powders contain, as expected, the phases Ni₂Al₃, NiAl₃ and an Al-eutectic. The Ti-doped powders contain an additional phase with the TiAl₃ DO₂₂ crystal structure. However, quantitative analysis of the XRD results indicate a far greater fraction of the TiAl₃ phase is present than could be accounted for by a simple mass balance on Ti. This appears to be a (Ti_xNi_1−x)Al₃ phase in which higher cooling rates favour small x (low Ti-site occupancy by Ti atoms). SEM and EDX analysis reveal that virtually all the available Ti is contained within the TiAl₃ phase, with negligible Ti dissolved in either the Ni₂Al₃ or NiAl₃ phases.